Semiconductor device and method of manufacturing the same

ABSTRACT

An isolation which is higher in a stepwise manner than an active area of a silicon substrate is formed. On the active area, an FET including a gate oxide film, a gate electrode, a gate protection film, sidewalls and the like is formed. An insulating film is deposited on the entire top surface of the substrate, and a resist film for exposing an area stretching over the active area, a part of the isolation and the gate protection film is formed on the insulating film. There is no need to provide an alignment margin for avoiding interference with the isolation and the like to a region where a connection hole is formed. Since the isolation is higher in a stepwise manner than the active area, the isolation is prevented from being removed by over-etch in the formation of a connection hole to come in contact with a portion where an impurity concentration is low in the active area. In this manner, the integration of a semiconductor device can be improved and an area occupied by the semiconductor device can be decreased without causing degradation of junction voltage resistance and increase of a junction leakage current in the semiconductor device.

BACKGROUND OF THE INVENTION

[0001] The present invention relates to a semiconductor device including transistors and connection between the transistors for constituting an LSI with high integration and a decreased area.

[0002] With the recent development of a semiconductor device with high integration and high performance, there are increasing demands for more refinement of the semiconductor device. The improvement of the conventional techniques cannot follow these demands, and novel techniques are unavoidably introduced in some technical fields. For example, as a method of forming an isolation, the LOCOS isolation method is conventionally adopted in view of its simpleness and low cost. Recently, however, it is considered that a trench buried type isolation (hereinafter referred to as the trench isolation) is more advantageous for manufacturing a refined semiconductor device.

[0003] Specifically, in the LOCOS isolation method, since selective oxidation is conducted, the so-called bird's beak occurs in the boundary with a mask for preventing the oxidation. As a result, the dimension of a transistor is changed because an insulating film of the isolation invades a transistor region against the actually designed mask dimension. This dimensional change is unallowable in the refinement of a semiconductor device after the 0.5 μm generation. Therefore, even in the mass-production techniques, the isolation forming method has started to be changed to the trench isolation method in which the dimensional change is very small. For example, IBM corporation has introduced the trench isolation structure as a 0.5 μm CMOS process for the mass-production of an MPU (IBM Journal of Research and Development, VOL. 39, No. 1/2, 1995, pp. 33-42).

[0004] Furthermore, in a semiconductor device mounting elements such as a MOSFET in an active area surrounded with an isolation, an insulating film is deposited on the active area, the isolation and a gate electrode, and a contact hole is formed by partly exposing the insulating film for connection between the active area and an interconnection member on a layer above the insulating film. This structure is known as a very common structure for the semiconductor device.

[0005]FIG. 17 is a sectional view for showing the structure of a conventional semiconductor device. In FIG. 17, a reference numeral 1 denotes a silicon substrate, a reference numeral 2 b denotes an isolation with a trench isolation structure which is made of a silicon oxide film and whose top surface is flattened so as to be at the same level as the top surface of the silicon substrate 1, a reference numeral 3 denotes a gate oxide film made of a silicon oxide film, a reference numeral 4 a denotes a polysilicon electrode working as a gate electrode, a reference numeral 4 b denotes a polysilicon interconnection formed simultaneously with the polysilicon electrode 4 a, a reference numeral 6 denotes a low-concentration source/drain region formed by doping the silicon substrate with an n-type impurity at a low concentration, a reference numeral 7 a denotes an electrode sidewall, a reference numeral 7 b denotes an interconnection sidewall, a reference numeral 8 denotes a high-concentration source/drain region formed by doping the silicon substrate with an n-type impurity at a high concentration, a reference numeral 12 denotes an insulating film made of a silicon oxide film, and a reference numeral 13 denotes a local interconnection made of a polysilicon film formed on the insulating film 12.

[0006] The local interconnection 13 is also filled within a connection hole 14 formed in a part of the insulating film 12, so as to be contacted with the source/drain region in the active area through the connection hole 14. In this case, the connection hole 14 is formed apart from the isolation 2 b by a predetermined distance. In other words, in the conventional layout rule for such a semiconductor device, there is a rule that the edge of a connection hole is previously located away from the boundary between the active area and the isolation region so as to prevent a part of the connection hole 14 from stretching over the isolation 2 b even when a mask alignment shift is caused in photolithography (this distance between the connection hole and the isolation is designated as an alignment margin).

[0007] However, in the structure of the semiconductor device as shown in FIG. 17, there arise problems in the attempts to further improve the integration for the following reason:

[0008] A distance La between the polysilicon electrode 4 a and the isolation 2 b is estimated as an index of the integration. In order to prevent the connection hole 14 from interfering the isolation 2 b as described above, the distance La is required to be 1.2 μm, namely, the sum of the diameter of the connection hole 14, that is, 0.5 μm, the width of the electrode sidewall 7 a, that is, 0.1 μm, the alignment margin from the polysilicon electrode 4 a, that is, 0.3 μm, and the alignment margin from the isolation 2 b , that is, 0.3 μm. A connection hole has attained a more and more refined diameter with the development of processing techniques, and also a gate length has been decreased as small as 0.3 μm or less. Still, the alignment margin in consideration of the mask alignment shift in the photolithography is required to be approximately 0.3 μm. Accordingly, as the gate length and the connection hole diameter are more refined, the proportion of the alignment margin is increased. This alignment margin has become an obstacle to the high integration.

[0009] Therefore, attempts have been made to form the connection hole 14 without considering the alignment margin in view of the alignment shift in the photolithography. Manufacturing procedures adopted in such a case will now be described by exemplifying an n-channel MOSFET referring to FIGS. 18(a) through 18(c).

[0010] First, as is shown in FIG. 18(a), after forming an isolation 2 b having the trench structure in a silicon substrate 1 doped with a p-type impurity (or p-type well), etch back or the like is conducted for flattening so as to place the surfaces of the isolation 2 b and the silicon substrate 1 at the same level. In an active area surrounded with the isolation 2 b, a gate oxide film 3, a polysilicon electrode 4 a serving as a gate electrode, an electrode sidewall 7 a, a low-concentration source/drain region 6 and a high-concentration source/drain region 8 are formed. On the isolation 2 b are disposed a polysilicon interconnection 4 b formed simultaneously with the polysilicon electrode 4 a and an interconnection sidewall 7 b. At this point, the top surface of the high-concentration source/drain region 8 in the active area is placed at the same level as the top surface of the isolation 2 b. Then, an insulating film 12 of a silicon oxide film is formed on the entire top surface of the substrate.

[0011] Next, as is shown in FIG. 18(b), a resist film 25 a used as a mask for forming a connection hole is formed on the insulating film 12, and the connection hole 14 is formed by, for example, dry etching.

[0012] Then, as is shown in FIG. 18(c), the resist film 25 a is removed, and a polysilicon film is deposited on the insulating film 12 and within the connection hole 14. The polysilicon film is then made into a desired pattern, thereby forming a local interconnection 13.

[0013] At this point, in the case where the alignment margin in view of the mask alignment shift in the formation of the connection hole 14 is not considered in estimating the distance La between the polysilicon electrode 4 a and the isolation 2 b, a part of the isolation 2 b is included in the connection hole 14 when the exposing area of the resist film 25 a is shifted toward the isolation 2 b due to the mask alignment shift in the photolithography. Through over-etch in conducting the dry etching of the insulating film 12, although the high-concentration source/drain region 8 made of the silicon substrate is not largely etched because of its small etching rate, the part of the isolation 2 b included in the connection hole 14 is selectively removed, resulting in forming a recess 40 in part of the connection hole 14. When the recess 40 in the connection hole 14 has a depth exceeding a given proportion to the depth of the high-concentration source/drain region 8, junction voltage resistance can be decreased and a junction leakage current can be increased because the concentration of the impurity in the high-concentration source/drain region 8 is low at that depth.

[0014] In order to prevent these phenomena, it is necessary to provide a predetermined alignment margin as is shown in the structure of FIG. 17 so as to prevent the connection hole 14 from interfering the isolation 2 b even when the alignment shift is caused in the lithography. In this manner, in the conventional layout rule for a semiconductor device, an alignment margin in view of the mask alignment shift in the photolithography is unavoidably provided.

[0015] Furthermore, a distance between the polysilicon electrode 4 a and the connection hole 14 is also required to be provided with an alignment margin. Otherwise, the connection hole 14 can interfere the polysilicon electrode 4 a due to the fluctuation caused in the manufacturing procedures, resulting in causing electric short-circuit between an upper layer interconnection buried in the connection hole and the gate electrode.

[0016] As described above, it is necessary to provide the connection hole 14 with margins for preventing the interference with other elements around the connection hole, which has become a large obstacle to the high integration of an LSI.

[0017] Also in the case where a semiconductor device having the so-called salicide structure is manufactured, the following problems are caused due to a recess formed in the isolation:

[0018]FIG. 19 is a sectional view for showing an example of a semiconductor device including the conventional trench isolation and a MOSFET having the salicide structure. As is shown in FIG. 19, a trench isolation 105 a is formed in a silicon substrate 101. In an active area surrounded with the isolation 105 a, a gate insulating film 103 a, a gate electrode 107 a, and electrode sidewalls 108 a on both side surfaces of the gate electrode 107 a are formed. Also in the active area, a low-concentration source/drain region 106 a and a high-concentration source/drain region 106 b are formed on both sides of the gate electrode 107 a. A channel stop region 115 is formed below the isolation 105 a. Furthermore, in areas of the silicon substrate 101 excluding the isolation 105 a and the active area, a gate interconnection 107 b made of the same polysilicon film as that for the gate electrode 107 a is formed with a gate insulating film 103 b sandwiched, and the gate interconnection 107 b is provided with interconnection sidewalls 108 b on its both side surfaces. On the gate electrode 107 a, the gate interconnection 107 b and the high-concentration source/drain region 106 b, an upper gate electrode 109 a, an upper gate interconnection 109 b and a source/drain electrode 109 c each made of silicide are respectively formed. Furthermore, this semiconductor device includes an interlayer insulating film 111 made of a silicon oxide film, a metallic interconnection 112 formed on the interlayer insulating film 111, and a contact member 113 (buried conductive layer) filled in a connection hole formed in the interlayer insulating film 111 for connecting the metallic interconnection 112 with the source/drain electrode 109 c.

[0019] Now, the manufacturing procedures for the semiconductor device including the conventional trench isolation and the MOSFET with the salicide structure shown in FIG. 19 will be described referring to FIGS. 20(a) through 20(e).

[0020] First, as is shown in FIG. 20(a), a silicon oxide film 116 and a silicon nitride film 117 are successively deposited on a silicon substrate 101, and a resist film 120 for exposing an isolation region and masking a transistor region is formed on the silicon nitride film 117. Then, by using the resist film 120 as a mask, etching is conducted, so as to selectively remove the silicon nitride film 116 and the silicon oxide film 117, and further etch the silicon substrate 101, thereby forming a trench 104. Then, impurity ions are injected into the bottom of the trench 104, thereby forming a channel stop region 115.

[0021] Then, as is shown in FIG. 20(b), a silicon oxide film (not shown) is deposited, and the entire top surface is flattened until the surface of the silicon nitride film 117 is exposed. Through this procedure, a trench isolation 105 a made of the silicon oxide film filled in the trench 104 is formed in the isolation region Reiso.

[0022] Next, as is shown in FIG. 20(c), after the silicon nitride film 117 and the silicon oxide film 116 are removed, a gate oxide film 103 is formed on the silicon substrate 101, and a polysilicon film 107 is deposited thereon. Then, a photoresist film 121 for exposing areas excluding a region for forming a gate is formed on the polysilicon film 107.

[0023] Then, as is shown in FIG. 20(d), by using the photoresist film 121 as a mask, dry etching is conducted, thereby selectively removing the polysilicon film 107 and the gate oxide film 103. Thus, a gate electrode 107 a of the MOSFET in the transistor region Refet and a gate interconnection 107 b stretching over the isolation 105 a and the silicon substrate 101 are formed. After removing the photoresist film 121, impurity ions are injected into the silicon substrate 101 by using the gate electrode 107 a as a mask, thereby forming a low-concentration 382 source/drain region 106 a. Then, a silicon oxide film 108 is deposited on the entire top surface of the substrate.

[0024] Next, as is shown in FIG. 20(e), the silicon oxide film 108 is anisotropically dry-etched, thereby forming electrode sidewalls 108 a and interconnection sidewalls 108 b on both side surfaces of the gate electrode 107 a and the gate interconnection 107 b, respectively. At this point, the gate oxide film 103 below the silicon oxide film 108 is simultaneously removed, and the gate oxide film 103 below the gate electrode 107 a alone remains. Then, impurity ions are diagonally injected by using the gate electrode 107 a and the electrode sidewalls 108 a as masks, thereby forming a high-concentration source/drain region 106 b. Then, after a Ti film is deposited on the entire top surface, high temperature annealing is conducted, thereby causing a reaction between the Ti film and the components made of silicon directly in contact with the Ti film. Thus, an upper gate electrode 109 a, an upper gate interconnection 109 b and a source/drain electrode 109 c made of silicide are formed.

[0025] The procedures to be conducted thereafter are omitted, but the semiconductor device including the MOSFET having the structure as shown in FIG. 19 can be ultimately manufactured. In FIG. 19, the metallic interconnection 112 is formed on the interlayer insulating film 111, and the metallic interconnection 112 is connected with the source/drain electrode 109 c through the contact member 113 including a W plug and the like filled in the contact hole.

[0026] When the aforementioned trench isolation structure is adopted, the dimensional change of the source/drain region can be suppressed because the bird's beak, that is, the oxide film invasion of an active area, which is caused in the LOCOS method where a thick silicon oxide film is formed by thermal oxidation, can be avoided. Furthermore, in the procedure shown in FIG. 20(c), the surfaces of the isolation 105 a and the silicon substrate 101 in the transistor region Refet are placed at the same level.

[0027] In such a semiconductor device having the trench type isolation, however, there arise the following problems:

[0028] When the procedures proceed from the state shown in FIG. 20(d) to the state shown in FIG. 20(e), the silicon oxide film 108 is anisotropically etched so as to form the sidewalls 108 a and 108 b. At this point, over-etch is required. Through this over-etch, the surface of the isolation 105 a is removed by some depth.

[0029] FIGS. 21(a) and 21(b) are enlarged sectional views around the boundary between the high-concentration source/drain region 106 b and the isolation 105 a after this over-etch.

[0030] As is shown in FIG. 21(a), between the procedures shown in FIGS. 20(d) and 20(e), the impurity ions are diagonally injected so as to form the high-concentration source/drain region 106 b . Through this ion injection, the high-concentration source/drain region 106 b is formed also below the edge of the isolation 105 a because the isolation 105 a is previously etched by some depth. Accordingly, the high-concentration source/drain region 106 b is brought closer to the channel stop region 115, resulting in causing the problems of degradation of the junction voltage resistance and increase of the junction leakage current.

[0031] In addition, as is shown in FIG. 21(b), in the case where the Ti film or the like is deposited on the high-concentration source/drain region 106 b so as to obtain the silicide layer through the reaction with the silicon below, the thus formed silicide layer can invade the interface between the silicon substrate 101 and the isolation 105 a with ease. As a result, a short-circuit current can be caused between the source/drain electrode 109 c made of silicide and the channel stop region 115.

SUMMARY OF THE INVENTION

[0032] The object of the present invention is improving the structure of an isolation, so as to prevent the problems caused because the edge of the isolation is trenched in etching for the formation of a connection hole or sidewalls.

[0033] In order to achieve the object, the invention proposes first and second semiconductor devices and first through third methods of manufacturing a semiconductor device as described below.

[0034] The first semiconductor device of this invention in which a semiconductor element is disposed in each of plural active areas in a semiconductor substrate comprises an isolation for surrounding and isolating each active area, the isolation having a top surface at a higher level than a surface of the active area and having a step portion in a boundary with the active area; an insulating film formed so as to stretch over each active area and the isolation; plural holes each formed by removing a portion of the insulating film disposed at least on the active area; plural buried conductive layers filled in the respective holes; and plural interconnection members formed on the insulating film so as to be connected with the respective active areas through the respective buried conductive layers.

[0035] Owing to this structure, in the case where a part of or all the holes are formed so as to stretch over the active areas and the isolation due to mask alignment shift in photolithography, a part of the isolation is removed by over-etch for ensuring the formation of the holes. In such a case, even when the top surface of the isolation is trenched to be lower than the surface of the active area, the depth of the holes formed in the isolation is small in the boundary with the active area because of the level difference between the top surface of the isolation and the surface of the active area. Accordingly, degradation of the junction voltage resistance and increase of the junction leakage current can be suppressed. Therefore, there is no need to provide a portion of the active area where each hole is formed with an alignment margin for avoiding the interference with the isolation caused by the mask alignment shift in the lithography. Thus, the area of the active area can be decreased, resulting in improving the integration of the semiconductor device.

[0036] In the first semiconductor device, at least a part of the plural holes can be formed so as to stretch over the active area and the isolation due to fluctuation in manufacturing procedures.

[0037] In other words, even when no margin for the mask alignment in the lithography is provided, the problems caused in the formation of the holes can be avoided.

[0038] Furthermore, the angle between a side surface of the step portion and the surface of the active area is preferably 70 degrees or more.

[0039] As a result, when the hole interferes the isolation, the part of the isolation included in the hole is definitely prevented from being etched through over-etch in the formation of the holes down to a depth where the impurity concentration is low in the active area.

[0040] The isolation is preferably a trench isolation made of an insulating material filled in a trench formed by trenching the semiconductor substrate by a predetermined depth.

[0041] This is because no bird's beak is caused in the trench isolation differently from a LOCOS film as described above, and hence, the trench isolation is suitable particularly for the high integration and refinement of the semiconductor device.

[0042] In the first semiconductor device, when the semiconductor element is a MISFET including a gate insulating film and a gate electrode formed on the active area; and source/drain regions formed in the active area on both sides of the gate electrode, the following preferred embodiments can be adopted:

[0043] The semiconductor device can further comprise a gate interconnection made of the same material as that for the gate electrode and formed on the isolation, each of the holes can be formed on an area including the source/drain region, the isolation and the gate interconnection, and the plural interconnection members can be connected with the gate interconnection on the isolation.

[0044] Owing to this configuration, in the case where the interconnection members work as local interconnections for connecting a gate interconnection on the isolation with the active area, there is no need to separately form holes in the insulating film on the gate interconnection and the insulating film on the active area. In addition, there is no need to provide the separate holes with alignment margins from the boundary between the active area and the isolation. Accordingly, the area of the isolation can also be decreased, resulting in largely improving the integration of the semiconductor device.

[0045] The semiconductor device can further comprise electrode sidewalls made of an insulating material and formed on both side surfaces of the gate electrode; and a step sidewall made of the same material as the insulating material for the electrode sidewalls and formed on the side surface of the step portion. In this semiconductor device, at least a part of the holes can be formed by also removing a portion of the insulating film disposed on the step sidewall.

[0046] Owing to this structure, the abrupt level difference between the surfaces of the isolation and the active area can be released by the step sidewall. Therefore, a residue is scarcely generated in patterning the interconnection members, and an upper interconnection is prevented from being disconnected and increasing in its resistance.

[0047] The semiconductor device can further comprise a gate protection film formed on the gate electrode, and at least a part of the holes can be formed so as to stretch over the source/drain region and at least a part of the gate protection film.

[0048] Owing to this structure, a part of the gate protection film included in the hole is removed by the over-etch in the formation of the holes. However, the gate electrode is protected by the gate protection film, and hence, electrical short circuit between the gate electrode and the interconnection member can be prevented. Accordingly, there is no need to provide an alignment margin from the gate electrode in the area where each hole is formed, resulting in further improving the integration.

[0049] The interconnection members can be first layer metallic interconnections, and the insulating film can be an interlayer insulating film disposed between the semiconductor substrate, and the first layer metallic interconnections. In this case, the semiconductor device preferably further comprises, between the interlayer insulating film and the semiconductor substrate an underlying film made of an insulating material having high etching selectivity against the interlayer insulating film.

[0050] The second semiconductor device of this invention in which a semiconductor element is disposed in each of plural active areas in a semiconductor substrate comprises a trench isolation for isolating and surrounding each active area, the trench isolation having a top surface at a higher level than a surface of the active area and having a step portion in a boundary with the active area; and a step sidewall formed on the side surface of the step portion of the trench isolation.

[0051] Owing to this structure, in the impurity ion injection for the formation of an impurity diffused layer of the semiconductor device, the step sidewall disposed at the edge of the trench isolation can prevent the impurity ions from being implanted below the edge of the isolation. Furthermore, also in adopting the structure including a source/drain electrode made of silicide, the step sidewall can prevent the silicide layer from being formed at a deep portion. Therefore, a short circuit current can be prevented from occurring between the source/drain electrode and a substrate region such as the channel stop region. In this manner, the function of the trench isolation to isolate each semiconductor element can be prevented from degrading.

[0052] In the second semiconductor device, the step sidewall is preferably made of an insulating material.

[0053] Also in the second semiconductor device, the semiconductor element can be a MISFET including a gate insulating film and a gate electrode formed on the active area; and source/drain regions formed in the active area on both sides of the gate electrode. This semiconductor device can be further provided with electrode sidewalls formed on both side surfaces of the gate electrode, and the step sidewall can be formed simultaneously with the electrode sidewalls.

[0054] Owing to this structure, the semiconductor elements can be a MISFET having the LDD structure suitable for the refinement. Because of this structure together with the trench isolation structure, the semiconductor device can attain a structure particularly suitable for the refinement and the high integration.

[0055] The first method of manufacturing a semiconductor device in which a semiconductor element is disposed in each of plural active areas in a semiconductor substrate comprises a first step of forming an isolation in a part of the semiconductor substrate, the isolation having a top surface at a higher level than a surface of the semiconductor substrate and having a step portion in a boundary with the surface of the semiconductor substrate; a second step of introducing an impurity at a high concentration into each active area of the semiconductor substrate surrounded by the isolation; a third step of forming an insulating film on the active area and the isolation; a fourth step of forming, on the insulating film, a masking member having an exposing area above an area at least including a portion of the active area where the impurity at the high concentration is introduced; a fifth step of conducting etching by using the masking member so as to selectively remove the insulating film and form holes; and a sixth step of forming a buried conductive layer by filling the holes with a conductive material and forming, on the insulating film, interconnection members to be connected with the buried conductive layer. In this method, in the fourth step, an alignment margin is not provided for preventing the exposing area of the masking member from including a portion above the isolation when mask shift is caused in photolithography.

[0056] In adopting this method, even when a part of the isolation is removed by over-etch in the fifth step so that the top surface of the isolation is etched to be lower than the surface of the active area, the depth of the holes formed in the isolation is small because of the level difference between the isolation and the active area. Accordingly, the decrease of the junction voltage resistance and the increase of the junction leakage current can be suppressed in the manufactured semiconductor device. In addition, the area of the active area can be decreased because no alignment margin from the isolation is provided, resulting in improving the integration of the manufactured semiconductor device.

[0057] In the first method of manufacturing a semiconductor device, the following preferred embodiments can be adopted:

[0058] The fifth step is preferably performed so as to satisfy the following inequality:

OE x a x (ER2/ER1)≦b+D x (2/10)

[0059] wherein “a” indicates a thickness of the insulating film, “b” indicates a level difference between the surface of the active area and the top surface of the isolation, “ER1” indicates an etching rate of the insulating film, “ER2” indicates an etching rate of the isolation, “D” indicates a depth of an impurity diffused layer in the active area, and “OE” indicates an over-etch ratio of the insulating film.

[0060] In adopting this method, even when a part of the isolation included in the hole is removed by over-etch in the formation of the holes, the bottom of the etched portion does not reach a portion where the impurity concentration is low in the active area. In other words, the top surface of the isolation is never placed at a lower level than the surface of the active area. Accordingly, the degradation of the junction voltage resistance and the increase of the junction leakage current can be definitely prevented in the manufactured semiconductor device.

[0061] When the semiconductor element is a MISFET, the method can further include, before the second step, a step of forming a gate insulating film on the active area, a step of depositing a conductive film on the gate insulating film and a step of forming a gate electrode by patterning the conducive film, and in the second step, the impurity at the high concentration is introduced so as to form a source/drain region. In such a case, the following preferred embodiments can be adopted.

[0062] The method can further comprise, after the step of depositing the conductive film, a step of depositing a protection insulating film on the conductive film, and in the step of forming the gate electrode, the conductive film as well as the protection insulating film are patterned, so as to form a gate protection film on the gate electrode. The fifth step can be performed so as to satisfy the following inequality:

OE x a x (ER3/ER1)<c

[0063] wherein “a” indicates a thickness of the insulating film, “c” indicates a thickness of the gate protection film, “ER1” indicates an etching rate of the insulating film, “ER3” indicates an etching rate of the gate protection film and “OE” indicates an over-etch ratio of the insulating film.

[0064] When this method is adopted, while the area of the active area is decreased by not providing an alignment margin for avoiding the interference between the connection hole and the gate electrode, the hole is prevented from reaching the gate electrode below the gate protection film.

[0065] In the fourth step, the masking member can be formed to be positioned without providing a margin for preventing the exposing area thereof from including a portion above the gate protection film even when the mask shift is caused in the photolithography.

[0066] Alternatively, in the fourth step, the masking member can be formed to be positioned with the exposing area thereof including at least a part of a portion above the gate protection film when the mask shift is not caused in the photolithography.

[0067] In the third step, an interlayer insulating film can be formed as the insulating film, and in the sixth step, first layer metallic interconnections can be formed as the interconnection members. In such a case, it is preferred that the interlayer insulating film is formed in the third step after an underlying film made of an insulating material having high etching selectivity against the interlayer insulating film is formed below the interlayer insulating film.

[0068] The second method of manufacturing a semiconductor device of this invention comprises a first step of forming an underlying insulating film on a semiconductor substrate; a second step of depositing an etching stopper film on the underlying insulating film; a third step of forming a trench by exposing a portion of the etching stopper film and the underlying insulating film where an isolation is to be formed and etching the semiconductor substrate in the exposed portion; a fourth step of depositing an insulating film for isolation on an entire top surface of the substrate, flattening the substrate until at least a surface of the etching stopper film is exposed, and forming a trench isolation in the trench so as to surround a transistor region; a fifth step of removing, by etching, at least the etching stopper film and the underlying insulating film, so as to expose a step portion between the transistor region and the trench isolation; a sixth step of depositing a gate oxide film and a conductive film on the substrate and making the conductive film into a pattern of at least a gate electrode; a seventh step of depositing an insulating film for sidewalls on the entire top surface of the substrate and anisotropically etching the insulating film for the sidewalls, so as to form electrode sidewalls and a step sidewall on side surfaces of the gate electrode and the step portion, respectively; and an eighth step of introducing an impurity into the semiconductor substrate in the transistor region on both sides of the gate electrode, so as to form source/drain regions.

[0069] When this method is adopted, since the step sidewall is formed between the semiconductor substrate in the transistor region and the trench isolation after completing the fifth step, the impurity ions are prevented from being implanted below the edge of the trench isolation in the impurity ion injection in the eighth step. Furthermore, also when an area in the vicinity of the surface of the source/drain region is subsequently silicified, the step sidewall made of the insulating film can prevent the silicide layer from being formed at a deep portion. Accordingly, not only the degradation of the junction voltage resistance and the current leakage but also the occurrence of a short circuit current between the source/drain electrode and the substrate region such as the channel stop region can be prevented.

[0070] In the second method of manufacturing a semiconductor device, the following preferred embodiments can be adopted:

[0071] In the second step, the thickness of the etching stopper film is preferably determined in consideration of an amount of over-etch in the seventh step, so that the step portion having a level difference with a predetermined size or more is exposed in the fifth step.

[0072] The method can further comprise, after completing the eighth step, a step of silicifying at least an area in the vicinity of the surface of the source/drain region.

[0073] The third method of manufacturing a semiconductor device of this invention comprises a first step of forming a gate insulating film on a semiconductor substrate; a second step of depositing a first conductive film to be formed into a gate electrode on the gate insulating film; a third step of forming a trench by exposing a portion of the first conductive film where a trench isolation is to be formed and etching the semiconductor substrate in the exposed portion; a fourth step of depositing an insulating film for isolation on an entire top surface of the substrate, flattening the substrate at least until a surface of the first conductive film is exposed, and forming the trench isolation in the trench so as to surround a transistor region; a fifth step of depositing a second conductive film to be formed into at least an upper gate electrode on the entire top surface of the flattened substrate; a sixth step of making the first and second conductive films into a pattern at least of the gate electrode and exposing a step portion between the transistor region and the trench isolation; a seventh step of depositing an insulating film for sidewalls on the entire top surface of the substrate and anisotropically etching the insulating film for the sidewalls, so as to form electrode sidewalls and a step sidewall on side surfaces of the gate electrode and the step portion, respectively; and an eighth step of introducing an impurity into the semiconductor substrate in the transistor region on both sides of the gate electrode, so as to form source/drain regions.

[0074] When this method is adopted, the same effects as those attained by the second method of manufacturing a semiconductor device can be attained. In addition, in the patterning process for the gate electrode, the top surface of the substrate is completely flat, and hence, the patterning accuracy for the gate electrode can be improved.

BRIEF DESCRIPTION OF THE DRAWINGS

[0075] FIGS. 1(a) through 1(d) are sectional views for showing manufacturing procedures of Embodiment 1 up to the formation of an isolation;

[0076] FIGS. 2(a) through 2(e) are sectional views for showing the manufacturing procedures of Embodiment 1 after the formation of the isolation;

[0077] FIGS. 3(a) through 3(f) are sectional views for showing manufacturing procedures of Embodiment 2 after the formation of an isolation;

[0078] FIGS. 4(a) through 4(c) are sectional views for showing manufacturing procedures of Embodiment 3;

[0079] FIGS. 5(a) through 5(c) are sectional views for showing manufacturing procedures of Embodiment 4;

[0080] FIGS. 6(a) through 6(f) are sectional views for showing manufacturing procedures of Embodiment 5;

[0081] FIGS. 7(a) through 7(c) are sectional views for showing manufacturing procedures of Embodiment 6;

[0082] FIGS. 8(a) through 8(c) are sectional views for showing manufacturing procedures of Embodiment 7 in which a comparatively thin insulating film of Embodiment 1 is replaced with a layered film and an interlayer insulating film;

[0083] FIGS. 9(a) through 9(c) are sectional views for showing the manufacturing procedures of Embodiment 7 in which a comparatively thin insulating film of Embodiment 2 is replaced with a layered film and an interlayer insulating film;

[0084] FIGS. 10(a) through 10(c) are sectional views for showing the manufacturing procedures of Embodiment 7 in which a comparatively thin insulating film of Embodiment 4 is replaced with a layered film and an interlayer insulating film;

[0085] FIGS. 11(a) through 11(c) are sectional views for showing the manufacturing procedures of Embodiment 7 in which a comparatively thin insulating film of Embodiment 5 is replaced with a layered film and an interlayer insulating film;

[0086]FIG. 12 is a sectional view for showing the structure of a semiconductor device of Embodiment 8;

[0087] FIGS. 13(a) through 13(e) are sectional views for showing manufacturing procedures for the semiconductor device of Embodiment 8;

[0088] FIGS. 14(a) through 14(e) are sectional views for showing manufacturing procedures for a semiconductor device of Embodiment 9;

[0089] FIGS. 15(a) through 15(f) are sectional views for showing manufacturing procedures for a semiconductor device of Embodiment 10;

[0090] FIGS. 16(a) through 16(e) are sectional views for showing manufacturing procedures for a semiconductor device of Embodiment 11;

[0091]FIG. 17 is a sectional view of a conventional semiconductor device in which the surfaces of an active area and a trench isolation are placed at the same level;

[0092] FIGS. 18(a) through 18(c) are sectional views for showing manufacturing procedures for the conventional semiconductor device of FIG. 17;

[0093]FIG. 19 is a sectional view of a conventional semiconductor device having a salicide structure and a trench isolation structure;

[0094] FIGS. 20(a) through 20(e) are sectional views for showing manufacturing procedures for the conventional semiconductor device of FIG. 19; and

[0095] FIGS. 21(a) and 21(b) are partial sectional views for showing problems, in a conventional semiconductor device having a trench isolation, occurring in an impurity ion injection process and a silicifying process, respectively.

DETAILED DESCRIPTION OF THE INVENTION

[0096] (Embodiment 1)

[0097] Embodiment 1 of the invention will now be described referring to FIGS. 1(a) through 1(d) and 2(a) through 2(e). In the manufacturing procedures of this embodiment, a connection hole for connecting an interconnection layer and a silicon substrate is designed to stretch over an active area and an isolation when alignment shift is not caused in photolithography.

[0098] In this embodiment, the isolation is formed as a trench isolation. Furthermore, interconnection to be formed above is assumed to be local interconnection in which an insulating film can be comparatively thin, but the embodiment is applicable also to general global interconnection formed on a thick interlayer insulating film.

[0099] First, as is shown in FIG. 1(a), a resist film 50 a having a predetermined pattern is formed on a p-type silicon substrate 1 (or a p-type well). The silicon substrate 1 is dry-etched by using the resist film 50 a as a mask, thereby forming a trench 51 with a depth of 1 μm.

[0100] Then, as is shown in FIG. 1(b), the resist film 50 a is removed, and then a silicon oxide film 2x is deposited on the entire top surface of the silicon substrate 1. Through this procedure, the previously formed trench 51 is filled with the silicon oxide film 2x.

[0101] Next, as is shown in FIG. 1(c), the silicon oxide film 2x on the silicon substrate 1 is removed by, for example, a CMP (chemical mechanical polishing) method or etch-back through dry etching using a resist film, and at the same time, a trench isolation 2 b is formed. At this point, the top surface of the silicon substrate 1 and the top surface of the isolation 2 b are flattened with no level difference therebetween.

[0102] Then, as is shown in FIG. 1(d), dry etching with high etch selectivity is conducted so as to etch the silicon substrate 1 alone by a thickness of 0.2 μm. Thus, a step portion which is higher in a stepwise manner than the top surface of the silicon substrate 1 by 0.2 μm is formed in the isolation 2 b. The level difference caused by the step portion is required to be sufficiently large in consideration of an amount of over-etch in etching a subsequently formed insulating film 12, and hence, the level difference is preferably equal to or larger than the thickness of the insulating film 12.

[0103] It is noted that the method of causing the level difference between the top surface of the isolation 2 b and the surface of the active area is not limited to that described above. For example, the level difference can be caused as follows: After an etching stopper film having a thickness corresponding to the level difference is previously deposited on the silicon substrate, a trench is formed and an insulating film for the trench isolation is deposited. Then, the entire top surface of the substrate is flattened by the CMP method or the like, and the etching stopper film is subsequently removed.

[0104] Next, As is shown in FIG. 2(a), after forming a gate oxide film 3 on the silicon substrate 1, a polysilicon film 4x is deposited on the entire top surface of the substrate.

[0105] Then, as is shown in FIG. 2(b), after forming a resist film (not shown) having a predetermined pattern on the polysilicon film 4x, dry etching is conducted so as to form a polysilicon electrode 4 a on the active area and a polysilicon interconnection 4 b on the isolation 2 b. Then, by using the gate electrode 4 a as a mask, n-type impurity ions are injected at a high concentration, thereby forming high-concentration source/drain regions 8 in the silicon substrate 1 on both sides of the polysilicon electrode 4 a.

[0106] After this, as is shown in FIG. 2(c), the insulating film 12 having a thickness of, for example, 0.15 μm is deposited, so that an interconnection subsequently formed above the insulating film (i.e., the local interconnection in this embodiment) can be electrically insulated from the polysilicon electrode, the polysilicon interconnection and the active area.

[0107] Next, as is shown in FIG. 2(d), a resist film 25 a having a pattern for forming a connection hole is formed on the insulating film 12. At this point, the exposing area of the resist film 25 a is positioned without an alignment margin for preventing interference with the isolation 2 b. In this embodiment, after the resist film 25 a is formed so that the exposing area stretches over the source/drain region 8, that is, the active area of a transistor, and the isolation 2 b, dry etching is conducted by using the resist film 25 a as a mask, thereby forming a connection hole 14 by removing the insulating film 12 in the exposing area of the resist film 25 a. At this point, when the insulating film 12 is, for example, 40% over-etched than its thickness of 0.15 μm in order to ensure the formation of the connection hole 14, the isolation 2 b in the exposing area of the resist film 25 a is etched by a thickness of approximately 0.06μm. However, in this embodiment, the step portion has a height of 0.2 μm, which is sufficiently larger than this etched amount, and hence, a recess where the top surface of the isolation 2 b is lower than the top surface of the silicon substrate 1 is never formed in any part of the connection hole 14.

[0108] Next, as is shown in FIG. 2(e), a polysilicon film is deposited on the entire top surface and is patterned, thereby forming the local interconnection 13. At this point, the local interconnection 13 is also formed within the connection hole 14, so as to be electrically connected with the source/drain region 8 serving as the active area.

[0109] In a semiconductor device formed in the aforementioned procedures, the top surface of the isolation 2 b is higher in a stepwise manner than the surface of the active area. Therefore, even when the isolation 2 b is removed by some amount by the over-etch in dry etching the insulating film 12, the isolation 2 b is prevented from being etched by a thickness exceeding the level difference caused by the step portion. Accordingly, when mask alignment is shifted in the photolithography, a recess with a depth reaching a certain depth of the source/drain region 8 is prevented from being formed in the connection hole 14. As a result, the conventional problems, that is, the degradation of the junction voltage resistance and the increase of the junction leakage current caused because of the low impurity concentration at a lower part of the active area of the silicon substrate corresponding to the sidewall of the recess, can be effectively prevented.

[0110] However, the level difference between the top surface of the isolation 2 b and the surface of the active area is not necessarily required to be larger than the thickness of the insulating film 12. The dimensions and materials of the respective components can be determined so as to satisfy the following inequality (1), wherein “a” denotes the thickness of the insulating film 12; “b” denotes the level difference between the top surface of the isolation 2 b and the surface of the active area; “ER1” denotes the etching rate of the insulating film 12; “ER2” denotes the etching rate of the isolation 2 b; “D” denotes the depth of an impurity diffused layer in the active area; and “OE” denotes the over-etch ratio of the insulating film 12 in the formation of the connection hole 14.

OE x a x (ER2/ER1)>b+D x (2/10)   (1)

[0111] As far as the inequality (1) is satisfied, even when a part of the isolation 2 b is removed to be at a lower level than the surface of the silicon substrate in the active area through the formation of the connection hole 14, so that the recess 40 as is shown in FIG. 18(c) is formed in a part of the connection hole 14, the bottom of the recess 40 is prevented from reaching the depth where the impurity concentration is low.

[0112] Since the alignment margin in view of the mask shift in the photolithography can be omitted, the following effects can be attained: When a distance Lb between the polysilicon electrode 4 a serving as the gate electrode and the isolation 2 b is estimated as an index of the integration, the distance Lb is 0.8 μm, namely, the sum of the diameter of the connection hole, 0.5 μm, and the alignment margin from the gate electrode, 0.3 μm. Thus, the distance Lb can be decreased by 0.4 μm as compared with the conventional distance La of 1.2 μm (shown in FIG. 17).

[0113] (Embodiment 2)

[0114] Embodiment 2 will now be described referring to FIGS. 3(a) through 3(f). In this embodiment, a connection hole for connecting an interconnection layer and a silicon substrate is formed so as to stretch over an active area and an isolation in the same manner as in Embodiment 1, and a step portion between the isolation and the active area is provided with a sidewall.

[0115] First, as is shown in FIGS. 3(a) and 3(b), an isolation 2 b whose top surface is higher in a stepwise manner than the surface of an active area by a predetermined level difference and a gate oxide film 3 are formed on a silicon substrate 1 in the same manner as described in Embodiment 1. Then, a polysilicon film 4x is deposited on the entire top surface.

[0116] Next, the polysilicon film 4x is patterned, thereby forming a polysilicon electrode 4 a and a polysilicon interconnection 4 b. The procedures conducted so far are identical to those adopted in Embodiment 1. Then, a silicon oxide film is deposited on the entire top surface and is subjected to anisotropic etching, thereby forming electrode sidewalls 7 a on both side surfaces of the polysilicon electrode 4 a and interconnection sidewalls 7 b on both side surfaces of the polysilicon interconnection 4 b. At the same time, a step sidewall 7 c is formed on the side surface of the step portion between the isolation 2 b and the active area. Each of the sidewalls has a width of, for example, approximately 0.1 μm. After forming the polysilicon electrode 4 a, an n-type impurity with a low concentration is ion-injected into the active area, so as to form a low-concentration source/drain region 6. After forming the electrode sidewalls 7 a, an n-type impurity with a high concentration is ion-injected into the active area, so as to form a high-concentration source/drain region 8. This is a generally adopted method of manufacturing a MOSFET having the so-called LDD structure.

[0117] Then, as is shown in FIGS. 3(d) through 3(f), the procedures as described in Embodiment 1 referring to FIGS. 2(c) through 2(e) are conducted, thereby forming an insulating film 12 and a local interconnection 13 thereon.

[0118] This embodiment can achieve the effect to improve the integration similarly to Embodiment 1. In addition, owing to the step sidewall 7 c, the abrupt level difference between the isolation 2 b and the active area can be released. As a result, the amount of residue generated in the formation of the local interconnection 13 by patterning the polysilicon film can be advantageously decreased, and disconnection of the local interconnection 13 and resistance increase thereof can also be prevented.

[0119] At this point, a distance Lc between the polysilicon electrode 4 a serving as a gate electrode and the isolation 2 b is estimated as an index of the integration. The distance Lc is 1.0 μm, namely, the sum of the diameter of the connection hole, 0.5 μm, the width of the electrode sidewall 7 a, 0.1 μm, the alignment margin from the polysilicon electrode 4 a, 0.3 μm, and the width of the step sidewall 7 c, 0.1 μm. Thus, the distance Lc can be decreased by 0.2 μm as compared with the conventional distance La of 1.2 μm (shown in FIG. 17).

[0120] (Embodiment 3)

[0121] Embodiment 3 will now be described referring to FIGS. 4(a) through 4(c).

[0122] In manufacturing procedures described in this embodiment, a connection hole is formed so as to stretch over an active area and an isolation only when mask alignment shift is caused in the photolithography.

[0123]FIG. 4(a) shows a state where the procedures described in Embodiment 2 referring to FIGS. 3(a) through 3(d) have been completed. Specifically, as is shown in FIG. 4(a), after an isolation 2 b with a top surface higher in a stepwise manner than the surface of an active area, a step sidewall 7 c on the side surface of the step portion of the isolation 2 b, a gate oxide film 3, a polysilicon electrode 4 a serving as a gate electrode, electrode sidewalls 7 a on both side surfaces of the polysilicon electrode 4 a, a low-concentration source/drain region 6, a high-concentration source/drain region 8, a polysilicon interconnection 4 b on the isolation 2 b, and interconnection sidewalls 7 b on both side surfaces of the polysilicon interconnection 4 b are formed, an insulating film 12 with a thickness of approximately 0.15 μm is formed on the entire top surface.

[0124] Next, as is shown in FIG. 4(b), a resist film 25 b for forming a connection hole is formed. At this point, in this embodiment, the resist film 25 b is formed so that the connection hole stretches over the active area (i.e., the high-concentration source/drain region 8) and the step sidewall 7 c when the mask alignment shift is not caused in the lithography. Then, the insulating film 12 is etched, thereby forming the connection hole 14 stretching over the active area and the step sidewall 7 c.

[0125] Then, as is shown in FIG. 4(c), a local interconnection 13 to be connected with the high-concentration source/drain region 8 is formed on the insulating film 12.

[0126] In the state shown in FIG. 4(b), the edge of the connection hole 14 can be shifted toward the isolation 2 b by a maximum of 0.3 μm due to the mask alignment shift in the lithography. In such a case, the resultant structure becomes that described in Embodiment 2 (shown in FIG. 3(e)). However, no recess is formed in the isolation 2 b within the connection hole 14 as described in Embodiments 1 and 2 even in such a case. Alternatively, even if a recess is formed, the problems of the degradation of the junction voltage resistance and the increase of the junction leakage current can be avoided as far as the dimensions and the like of the respective components are determined so as to satisfy the inequality (1).

[0127] Also in this embodiment, a distance Lc between the polysilicon electrode 4 a and the isolation 2 b is estimated as an index of the integration. Similarly to Embodiment 2, the distance Lc is 1.0 μm, namely, the sum of the diameter of the connection hole, 0.5 μm, the width of the electrode sidewall 7 a, 0.1 μm, the alignment margin from the polysilicon electrode 4 a, 0.3 μm, and the width of the step sidewall 7 c, 0.1 μm. Thus, the distance Lc can be decreased by 0.2 μm as compared with the conventional distance La of 1.2 μm.

[0128] (Embodiment 4)

[0129] Embodiment 4 will now be described referring to FIGS. 5(a) through 5(c). In manufacturing procedures described in this embodiment, a connection hole for connecting an interconnection layer and a silicon substrate is formed so as to stretch over an active area and a polysilicon interconnection on an isolation.

[0130]FIG. 5(a) shows the state where the procedures described in Embodiment 2 referring to FIGS. 3(a) through 3(d) have been completed. Specifically, as is shown in FIG. 5(a), after an isolation 2 b with a top surface higher in a stepwise manner than the surface of the active area, a step sidewall 7 c on the side surface of the step portion of the isolation 2 b, a gate oxide film 3, a polysilicon electrode 4 a serving as a gate electrode, electrode sidewalls 7 a on both side surfaces of the polysilicon electrode 4 a, a low-concentration source/drain region 6, a high-concentration source/drain region 8, a polysilicon interconnection 4 b on the isolation 2 b, and interconnection sidewalls 7 b on both side surfaces of the polysilicon interconnection 4 b are formed, an insulating film 12 with a thickness of approximately 0.15 μm is formed on the entire top surface.

[0131] Next, as is shown in FIG. 5(b), a resist film 25 c for forming a connection hole is formed. In this embodiment, the resist film 25 c is formed with its exposing area stretching over the active area (i. e., the high-concentration source/drain region 8) and the polysilicon interconnection 4 b on the isolation 2 b when the mask alignment shift is not caused in the lithography. Then, the insulating film 12 is etched, thereby forming the connection hole 14 stretching over the high-concentration source/drain region 8, the isolation 2 b and the polysilicon interconnection 4 b.

[0132] Then, as is shown in FIG. 5(c), a local interconnection 13 to be connected with the high-concentration source/drain region 8 and the polysilicon interconnection 4 b is formed on the insulating film 12.

[0133] When the high-concentration source/drain region 8 is to be electrically connected with the polysilicon interconnection 4 b serving as a gate interconnection formed on the isolation 2 b in the conventional manufacturing procedures, a connection hole formed on the high-concentration source/drain region 8 and another connection hole formed on the polysilicon interconnection 4 b are required to be positioned in consideration of alignment margins from the boundaries with the high-concentration source/drain region 8 and the isolation 2 b, respectively. In contrast, in this embodiment, the interconnection member can be connected with the high-concentration source/drain region 8 and the polysilicon electrode 4 b through one connection hole 14 without consideration of the alignment margins. In addition, as described in Embodiments 1 through 3, the problems of the degradation of the junction voltage resistance and the increase of the junction leakage current can be prevented from being caused through the over-etch in etching the insulating film 12.

[0134] In this embodiment, the interconnection on the isolation 2 b is made of a polysilicon film, but another conductive material or an interconnection on a layer different from the polysilicon electrode can be used instead.

[0135] (Embodiment 5)

[0136] Embodiment 5 will now be described referring to FIGS. 6(a) through 6(f). In manufacturing procedures described in this embodiment, a connection hole for connecting an interconnection layer and a silicon substrate is formed so as to stretch over an active area, a gate electrode and an isolation.

[0137] First, as is shown in FIG. 6(a), an isolation 2 b with a top surface higher in a stepwise manner than the surface of a p-type silicon substrate 1 is formed.

[0138] Next, as is shown in FIG. 6(b), a polysilicon film 4x with a thickness of 0.2 μm is deposited on the entire top surface, and a silicon oxide film 15x for gate protection with a thickness of approximately 0.15 μm is deposited on the polysilicon film 4x. At this point, the thickness of the silicon oxide film 15x for gate protection is required to be sufficiently large in consideration of an amount of over-etch to be removed in etching a subsequently formed insulating film 12. In this embodiment, the thickness of the silicon oxide film 15x is substantially the same as that of the insulating film 12.

[0139] Then, as is shown in FIGS. 6(c) and 6(d), the procedures as described in Embodiment 2 referring to FIGS. 3(c) and 3(d) are conducted. Thus, after a polysilicon electrode 4 a and a gate protection film 15 a together serving as a gate electrode, electrode sidewalls 7 a on both side surfaces of the polysilicon electrode 4 a and the gate protection film 15 a, a low-concentration source/drain region 6, a high-concentration source/drain region 8, a polysilicon interconnection 4 b and an interconnection protection film 15 b on the isolation 2 b, interconnection sidewalls 7 b on both side surfaces of the polysilicon interconnection 4 b and the interconnection protection film 15 b and a step sidewall 7 c are formed, the insulating film 12 with a thickness of approximately 0.15 μm is formed on the entire top surface.

[0140] Next, as is shown in FIG. 6(e), a resist film 25 d for forming a connection hole is formed. At this point, in this embodiment, the resist film 25 d is formed so that the connection hole stretches over the polysilicon electrode 4 a, the high-concentration source/drain region 8 serving as the active area and the isolation 2 b when the mask alignment shift is not caused in the lithography. Accordingly, when the alignment shift is not caused, the exposing area of the resist film 25 d stretches also over a part of the polysilicon electrode 4 a. Then, the insulating film 12 is patterned by dry etching. At this point, a part of the isolation 2 b and the gate protection film 15 a in the exposing area of the resist film 25 d are also removed by some amount by the over-etch in the dry etching of the insulating film 12. However, the connection hole 14 never reaches the polysilicon electrode 4 a.

[0141] Then, as is shown in FIG. 6(f), a polysilicon film is deposited on the entire top surface and then patterned, thereby forming a local interconnection 13 to be connected with the high-concentration source/drain region 8.

[0142] In this embodiment, the problems of the degradation of the junction voltage resistance and the increase of the junction leakage current can be avoided as in the aforementioned embodiments even when the insulating film 12 is 40% over-etched than its thickness of 0.15 μm in order to form the connection hole 14

[0143] In particular in this embodiment, the connection hole 14 stretches also over the polysilicon electrode 4 a when the alignment shift is not caused in the lithography. Therefore, when the insulating film 12 is, for example, 40% over-etched than its thickness of 0.15 μm in the dry etching thereof, although a part of the gate protection film 15 a is etched by a thickness of approximately 0.06 μm. However, the conventional problem of the electric short circuit with an interconnection on an upper layer through the connection hole can be avoided since the thickness of the gate protection film 15 a is 0.15 μm, which is sufficiently larger than 0.06 μm.

[0144] It is noted that the thickness of the gate protection film 15 a can be determined as follows: The dimensions and materials of the respective components are determined so as to satisfy the following inequality (2), wherein “a” denotes the thickness of the insulating film 12; “c” denotes the thickness of the gate protection film 4 a, “ER1” denotes the etching rate of the insulating film 12; “ER3” denotes the etching rate of the gate protection film 4 a; and “OE” denotes the over-etch ratio of the insulating film 12 in the formation of the connection hole 14:

OE x a x (ER3/ER1)<c   (2)

[0145] At this point, a distance Ld between the polysilicon electrode 4 a serving as the gate electrode and the isolation 2 b is estimated as an index of the integration. The distance Ld is 0.7 μm, namely, the sum of the diameter of the connection hole, 0.5 μm, the width of the electrode sidewall 7 a, 0.1 μm, and the width of the step sidewall 7 c, 0.1 μm. Thus, the distance Ld can be decreased by 0.5 μm as compared with the conventional distance of 1.2 μm.

[0146] (Embodiment 6)

[0147] Embodiment 6 will now be described referring to FIGS. 7(a) through 7(c). In manufacturing procedures described in this embodiment, a connection hole for connecting an interconnection layer and a silicon substrate is formed so as to stretch over an active area, an electrode sidewall and an isolation when the alignment shift is not caused, and is formed so as to stretch also over a polysilicon electrode only when the alignment shift is caused.

[0148]FIG. 7(a) shows the state where the procedures described in Embodiment 5 referring to FIGS. 6(a) through 6(d) have been completed. Specifically in FIG. 7(a), after an isolation 2 b having a top surface higher in a stepwise manner than the surface of the active area, a step sidewall 7 c on the side surface of the step portion of the isolation 2 b, a gate oxide film 3, a polysilicon electrode 4 a serving as a gate electrode, a gate protection film 15 a on the polysilicon electrode 4 a, electrode sidewalls 7 a on both side surfaces of the polysilicon electrode 4 a and the gate protection film 15 a, a low-concentration source/drain region 6, a high-concentration source/drain region 8, a polysilicon interconnection 4 b on the isolation 2 b, an interconnection protection film 15 b on the polysilicon interconnection 4 b, and interconnection sidewalls 7 b on both side surfaces of the polysilicon interconnection 4 b and the interconnection protection film 15 b are formed, an insulating film 12 having a thickness of approximately 0.15 μm is formed on the entire top surface.

[0149] Next, as is shown in FIG. 7(b), a resist film 25 e having a pattern for forming a connection hole is formed. At this point, in this embodiment, the resist film 25 e is formed so that its exposing area can expose at least the step sidewall 7 c and the high-concentration source/drain region 8 serving as the active area and stretches also over the electrode sidewall 7 a.

[0150] Then, a polysilicon film is deposited on the entire top surface and patterned, thereby forming a local interconnection 13 to be connected with the high-concentration source/drain region 8.

[0151] In the procedure shown in FIG. 7(b) of this embodiment, when the exposing area of the resist film 25 e is shifted by, for example, a maximum of 0.3 μm due to the alignment shift in the lithography, the connection hole 14 is formed so as to stretch also over a part of the polysilicon electrode 4 a. When the exposing area of the resist film 25 e is shifted in the reverse direction, the connection hole 14 is formed so as to stretch also over a part of the isolation 2 b. However, in either case, the junction voltage at the edge of the isolation 2 b is prevented from degrading and the junction leakage current is prevented from increasing as far as the dimensions and the like of the respective components are determined so as to satisfy the inequalities (1) and (2). In addition, an electrical short circuit between an interconnection member such as the local interconnection and the polysilicon electrode 4 a can be avoided.

[0152] At this point, a distance Le between the polysilicon electrode 4 a serving as the gate electrode and the isolation 2 b is estimated as an index of the integration. Similarly to Embodiment 5, the distance Le is 0.7 μm, namely, the sum of the diameter of the connection hole, 0.5 μm, the width of the electrode sidewall 7 a, 0.1 μm, and the width of the step sidewall 7 c, 0.1 μm. Thus, the distance Le can be decreased by 0.5 μm as compared with the conventional distance of 1.2 μm.

[0153] In each of the aforementioned embodiments, the local interconnection is adopted as the interconnection member so as to make the insulating film 12 comparatively thin. However, each embodiment can be applied to an interconnection member using a general global interconnection formed with an interlayer insulating film sandwiched. When the global interconnection is adopted, the interlayer insulating film is comparatively thick. Therefore, the effects of the embodiments can be similarly attained by decreasing the over-etch ratio of the interlayer insulating film in the formation of the connection hole or by increasing the level difference between the top surface of the isolation and the surface of the active area. This will be described in more detail in Embodiment 7 below.

[0154] Furthermore, when the isolation 2 b and the gate protection film 15 a used in Embodiment 5 or 6 are made of a material having a smaller etching rate than the material for the insulating film 12 against the etching for forming the connection hole, the semiconductor device can be manufactured with more ease.

[0155] In addition, when the insulating film 12 in each of the aforementioned embodiments has a multilayered structure including at least one lower layer made of a material having a smaller etching rate against the etching for forming the connection hole, the semiconductor device can be manufactured with more ease.

[0156] (Embodiment 7)

[0157] Embodiment 7 will now be described in which an interconnection layer formed on a thick interlayer insulating film is connected with an active area of a semiconductor substrate through a contact hole formed on the interlayer insulating film.

[0158] FIGS. 8(a) through 8(c) are sectional views for showing procedures for forming a layered film 10 and an interlayer insulating film 11 instead of the comparatively thin insulating film 12 of Embodiment 1. As is shown in FIG. 8(a), after conducting the procedures shown in FIGS. 1(a) through l(d) and 2(a) through 2(c), a layered film 10 including a silicon oxide film 10 a with a thickness of approximately 70 nm and a silicon nitride film 10 b with a thickness of approximately 80 nm is formed on the entire top surface of the substrate. Then, an interlayer insulating film 11 of a silicon oxide film with a thickness of approximately 600 nm is deposited thereon. Next, a resist film 25 a having a pattern for forming a contact hole is formed on the interlayer insulating film 11. At this point, the exposing area of the resist film 25 a is positioned without an alignment margin for avoiding interference with an isolation 2 b. In FIG. 8(a), the resist film 25 a is formed so that the exposing area stretches over a source/drain region 8 serving as the active area of a transistor and the isolation 2 b.

[0159] Next, as is shown in FIG. 8(b), etching is conducted by using the resist film 25 a as a mask, thereby selectively removing the interlayer insulating 25 a and the layered film 10. Thus, a contact hole 20 stretching over the isolation 2 b and the active area is formed.

[0160] Then, as is shown in FIG. 8(c), a plug underlying film 21 made of a TiN/Ti film and a W plug 22 are deposited within the contact hole 20 by selective CVD. Furthermore, an aluminum alloy film is deposited on the entire top surface of the substrate and the aluminum alloy film is patterned, thereby forming a first layer metallic interconnection 23. At this point, the first layer metallic interconnection 23 is electrically connected with the source/drain region 8 serving as the active area through the W plug 22 and the plug underlying film 23 filled in the contact hole 20.

[0161] FIGS. 9(a) through 9(c) are sectional views for showing procedures for forming a layered film 10 and an interlayer insulating film 11 instead of the comparatively thin insulating film 12 of Embodiment 2. In these manufacturing procedures, a procedure for forming sidewalls 7 a through 7 c is added to the manufacturing procedures shown in FIGS. 8(a) through 8(c), so as to manufacture a transistor having the LDD structure.

[0162] FIGS. 10(a) through 10(c) are sectional views for showing procedures for forming a layered film 10 and an interlayer insulating film 11 instead of the comparatively thin insulating film 12 of Embodiment 4. In the procedure shown in FIG. 10(a), a resist film 25 c having its exposing area stretching over the active area and the gate interconnection 4 b is formed on the interlayer insulating film 11. Thereafter, the same procedures as those shown in FIGS. 8(b) and 8(c) are conducted.

[0163] FIGS. 11(a) through 11(c) are sectional views for showing procedures for forming a layered film 10 and an interlayer insulating film 11 instead of the comparatively thin insulating film 12 of Embodiment 5. In the procedure shown in FIG. 11(a), a gate protection silicon oxide film 15 a is formed on a gate electrode 4 a, and the layered film 10 and the interlayer insulating film 11 are formed thereon. Then, a resist film 25 d having its exposing area stretching over the isolation, the active area and the gate electrode 4 a is formed on the interlayer insulating film 11. Thereafter, the same procedures as those shown in FIGS. 8(b) and 8(c) are conducted.

[0164] In each of the procedures shown in FIGS. 8(b), 9(b), 10(b) and 11(b), the silicon nitride film 10 b having high etching selectivity against the silicon oxide film is formed below the interlayer insulating film 11. Therefore, the silicon nitride film 10 b is prevented from being completely removed by the over-etch in etching the interlayer insulating film 11. When the silicon nitride film 10 b is to be removed from the layered film 10, the silicon oxide film 10 a is prevented from being completely removed since the etching selectivity between the silicon nitride film 10 b and the silicon oxide film 10 a below is high. Furthermore, since the silicon oxide film 10 a has a thickness of approximately 70 nm, which is smaller than the level difference of 0.2 μm between the isolation and the active area, the isolation 2 b is prevented from being etched to be lower than the surface of the active area by the over-etch in etching the silicon oxide film 10 a. In other words, a recess where the top surface of the isolation 2 b is lower than the surface of the silicon substrate is never formed in any part of the contact hole 20. Accordingly, in the formation of the contact hole for electrically connecting the interconnection layer formed on the interlayer insulating film and the active area of the semiconductor substrate, the same effects as those described in the aforementioned embodiments can be attained.

[0165] However, the underlying film below the interlayer insulating film can be omitted in this embodiment. Even when it is omitted, since the step portion is formed between the top surface of the isolation and the surface of the active area, the isolation cannot be etched to be lower than the surface of the active area in the formation of the contact hole. Thus, the degradation of the junction voltage resistance the increase of the junction leakage current can be prevented as much as possible.

[0166] (Embodiment 8)

[0167] Embodiment 8 will now be described referring to FIGS. 12 and 13(a) through 13(e). FIG. 12 is a sectional view showing the structure of a semiconductor device of this embodiment, and FIGS. 13(a) through 13(e) are sectional views for showing manufacturing procedures for the semiconductor device having the structure shown in FIG. 12.

[0168] As is shown in FIG. 12, in a silicon substrate (or well) 1 of one conductivity type, a trench isolation 2 b is formed in an isolation region Reiso for partitioning an area in the vicinity of the surface of the silicon substrate 1 into a plurality of transistor regions Refet. The top surface of the isolation 2 b is sufficiently higher than the surface of the silicon substrate 1 in each transistor region Refet, and a step portion with a predetermined level difference is formed between the isolation 2 b and the transistor region Refet. This isolation 2 b is formed by filling a trench formed in the silicon substrate 1 with an insulating material as described below. Furthermore, a channel stop region 60 of the same conductivity type as that of the silicon substrate 1 is formed at least below the isolation 2 b.

[0169] In each transistor region Refet partitioned by the isolation 2 b is formed a MOS transistor including a gate electrode 4 a, a gate oxide film 3, electrode sidewalls 7 a, a low-concentration source/drain region 6 and a high-concentration source/drain region 8. Also, on the silicon substrate 1 excluding the transistor regions Refet and on the isolation 2 b, a gate interconnection 4 b formed simultaneously with the gate electrode 4 a and interconnection sidewalls 7 b are formed. Furthermore, an upper gate electrode 9 a, an upper gate interconnection 9 b and a source/drain electrode 9 c each made of titanium silicide (TiSi₂) are formed on the gate electrode 4 a, the gate interconnection 4 b and the high-concentration source/drain region 8, respectively.

[0170] This embodiment is characterized by a step sidewall 7 c formed on the side surface of the step portion of the isolation 2 b simultaneously with the electrode sidewalls 7 a and the interconnection sidewalls 7 b. A part of the step sidewall 7 c is communicated with the electrode sidewalls 7 a and the interconnection sidewalls 7 b.

[0171] Furthermore, on the entire top surface of the substrate bearing the isolation 2 b, the gate electrode 4 a and the like, an interlayer insulating film 11 and a first layer metallic interconnection 23 are formed. The first layer metallic interconnection 23 is connected with the upper gate electrode 9 a and the source/drain electrode 9 c in the transistor region through a W plug 22.

[0172] Now, the manufacturing procedures for realizing the structure shown in FIG. 12 will be described referring to FIGS. 13(a) through 13(e).

[0173] First, as is shown in FIG. 13(a), a silicon oxide film 52 and a silicon nitride film 53 are deposited on a silicon substrate 1. Then, a resist film 50 a for exposing the isolation regions Reiso and masking the transistor regions Refet is formed on the silicon nitride film 53. After this, etching is conducted by using the resist film 50 a as a mask, so as to selectively remove the silicon nitride film 53 and the silicon oxide film 52 and further etch the silicon substrate 1, thereby forming a trench 51. At this point, differently from the conventional method of forming a trench, the silicon nitride film 53 has a thickness as large as approximately 150 through 200 nm. However, the silicon oxide film 52 has a thickness of 10 through 20 nm as in the conventional method. The depth of the trench 51 can be approximately 500 nm also as in the conventional method. Then, impurity ions of a conductivity type different from that of an impurity to be injected into a subsequently formed source/drain region are injected, thereby forming a channel stop region 60.

[0174] Next, as is shown in FIG. 13(b), after removing the resist film 50 a, a silicon oxide film (not shown) is deposited so as to have a sufficient thickness larger than the sum of the depth of the trench 51 and the thickness of the remaining silicon nitride film 53, namely, the height from the bottom of the trench 51 to the top surface of the silicon nitride film 53. Then, the silicon oxide film is removed by the CMP method so as to expose the surface of the silicon nitride film 53, thereby flattening the entire top surface of the substrate. Through this procedure, a trench isolation 2 b made of the silicon oxide film is formed in the isolation region Reiso. The flattening method to be adopted is not limited to that described above but the surface can be flattened by etch-back using a resist film having a reverse pattern to the pattern of the transistor region Refet.

[0175] Then, the silicon nitride film 53 is removed by using a phosphoric acid boiling solution or the like and the silicon oxide film 52 is removed by using a hydrofluoric acid type wet etching solution or the like, so as to expose the surface of the silicon substrate 1 in the transistor region Refet, which procedures are not shown in the drawing. At this point, a step portion having a sufficient level difference between the surface of the silicon substrate 1 in the transistor region Refet and the top surface of the isolation 2 b is exposed characteristically in this embodiment. The level difference is set at approximately 50 through 100 nm in consideration of the amount of over-etch in a procedure for forming sidewalls described below. However, in order to effectively achieve the effects of this embodiment, the thickness of an insulating film for the sidewall and the amount of over-etch are required to be appropriately determined in the subsequent procedure for forming the sidewalls.

[0176] Then, as is shown in FIG. 13(c), a polysilicon film 4 is deposited on the silicon substrate 1 and the isolation 2 b, and the resist film 50 b for exposing an area excluding the areas for a gate electrode and a gate interconnection is formed thereon. Then, the dry etching is conducted by using the resist film 50 b as a mask, thereby forming the gate electrode 4 a and the gate interconnection 4 b, which procedure is not shown in the drawing.

[0177] Next, as is shown in FIG. 13(d), by using the gate electrode 4 a as a mask, impurity ions at a low concentration are injected, thereby forming a low-concentration source/drain region 6. Then, an insulating film 7 (a silicon oxide film) is deposited on the entire top surface of the substrate.

[0178] Then, as is shown in FIG. 13(e), the insulating film 7 is anisotropically etched, thereby forming the electrode sidewalls 7 a on the both side surfaces of the gate electrode 4 a and interconnection sidewalls 7 b on the both side surfaces of the gate interconnection 4 b. At the same time, a step sidewall 7 c is formed on the side surface of the step portion between the silicon substrate 1 in the transistor region Refet and the isolation 2 b. After forming these sidewalls, impurity ions are injected, thereby forming the high-concentration source/drain region 8. Also at this point, the step portion between the silicon substrate 1 in the transistor region Refet and the isolation 2 b has the sufficient level difference.

[0179] Although the procedures thereafter are not shown in the drawing, an upper gate electrode 9 a, an upper gate interconnection 9 b and a source/drain electrode 9 c are formed by a silicifying procedure, an interlayer insulating film 11 is deposited and a contact hole is formed, and then the contact hole is filled with a metal, and a first layer metallic interconnection 12 is formed. IIn this manner, the MOS transistor having the trench isolation structure as shown in FIG. 12 is manufactured.

[0180] In the aforementioned procedures, the electrode sidewalls 7 a and the like are formed in order to manufacture a transistor with the LDD structure. However, the electrode sidewalls 7 a and the like can be formed in a transistor having the so-called pocket injection structure, in which a punch-through stopper is formed by injecting an impurity of a different conductivity type into an area between the source/drain region and the channel region. Therefore, this embodiment is applicable to such a transistor having the pocket injection structure.

[0181] In manufacturing a MOS transistor having a gate length of 1 μm or less as in this embodiment, it is necessary to form the electrode sidewalls 7 a on the side surfaces of the gate electrode 4 a in order to provide the transistor with the LDD structure or the pocket injection structure in which the short channel effect can be suppressed and the reliability of the transistor can be ensured. The thickness of the electrode sidewall 7 a depends upon the characteristics of a device to be manufactured. Since the sidewall is formed by dry etching with high anisotropy, its thickness can be controlled substantially only by controlling the thickness of the film to be deposited. However, 10% through 30% over-etch is generally conducted in consideration of the fluctuation in the etching rate in the wafer and the fluctuation in the thickness of the deposited film. For example, when the electrode sidewall 7 a is formed out of an insulating film with a thickness of 100 nm, the etching is conducted for a time period corresponding to time required for removing an insulating film with a thickness of 110 through 130 nm.

[0182] At this point, the isolation 2 b made of an oxide film is etched at higher selectivity than the silicon substrate 1 in the transistor region Refet, and hence, the isolation 2 b is removed by a thickness of, for example, 10 through 30 nm. Therefore, in the conventional structure, the surface of the isolation 105 a becomes lower than the surface of the silicon substrate 101 as is shown in FIGS. 21(a) and 21(b), resulting in causing the aforementioned problems. In contrast, in the state of this embodiment shown in FIG. 13(d), the isolation 2 b has the step portion whose surface is higher than the surface of the silicon substrate in the transistor region Refet, resulting in effectively preventing the problems. In other words, even when the impurity ions are diagonally injected for the formation of the high-concentration source/drain region 8, the impurity ions are prevented from being implanted below the edge of the isolation 2 b because the step portion of the isolation 2 b has a sufficient level difference. Accordingly, a distance between the high-concentration source/drain region 8 and the channel stop region 60 can be made substantially constant, thereby preventing the degradation of the junction voltage resistance and the increase of the junction leakage. Furthermore, in the formation of the source/drain electrode 9 c of silicide on the high-concentration source/drain region 8, the step sidewall 7 c effectively prevents the silicide layer from being formed in the boundary between the silicon substrate 1 and the isolation 2 b. Therefore, it is possible to effectively prevent a short circuit current from occurring between the source/drain electrode 9 c and the channel stop region 60.

[0183] In order to effectively achieve the aforementioned effects in this embodiment, however, the level difference caused by the step portion is-preferably larger than the amount of over-etch in the formation of the sidewalls, that is, 10 through 30 nm. Furthermore, in practical use, after the formation of the isolation 2 b, other procedures are conducted in which the thickness of the silicon oxide film used as the isolation 2 b is decreased, such as a procedure for removing the silicon oxide film 52. Therefore, it is preferred that the step portion is previously formed so as to have a sufficiently large level difference also in consideration of the afterward decreased amount. Accordingly, the lower limit of the thickness of the silicon nitride film 53 deposited in the procedure shown in FIG. 13(a) is determined on the basis of the amount of over-etch and the etched amount in the procedure for removing the silicon oxide film 52.

[0184] In this embodiment, the silicon nitride film 53 is used as an etching mask for forming the trench 51. This film can be made of any material which has large etching selectivity against the silicon oxide film, and can be, for example, a polysilicon film or the like.

[0185] This embodiment exemplifies the so-called salicide structure in which the upper gate electrode 9 a and the source/drain electrode 9 c are simultaneously silicified in a self-aligned manner for attaining low resistance. It goes without saying that the embodiment is applicable to a structure in which a gate electrode is previously formed as a polycide electrode and a source/drain electrode alone is silicified afterward.

[0186] (Embodiment 9)

[0187] Embodiment 9 will now be described referring to FIGS. 14(a) through 14(e). This embodiment is different from Embodiment 8 in that a gate oxide film and a polysilicon film serving as a gate electrode are deposited before forming a trench isolation.

[0188] First, as is shown in FIG. 14(a), a gate oxide film 3 and a polysilicon film 4 serving as a gate electrode of a MOS transistor are successively deposited on a silicon substrate 1. A resist film 50 a for exposing an isolation region Reiso and masking a transistor region Refet is patterned. By using the resist film 50 a as a mask, the polysilicon film 4 and the gate oxide film 3 are selectively removed, and further the silicon substrate 1 is etched, thereby forming a trench 51 serving as the isolation region. At this point, differently from the conventional method of forming a trench, the thickness of the polysilicon film 4 is set at 150 through 200 nm, that is, substantially the same thickness as that of the silicon nitride film used in Embodiment 8. The gate oxide film 3 has a thickness of 10 through 20 nm. The depth of the trench 51 is approximately 500 nm. Then, impurity ions of a different conductivity type from that of an impurity to be injected into a source/drain region formed afterward are injected, thereby forming a channel stop region 60.

[0189] Then, after removing the resist film 50 a, a silicon oxide film 2 (not shown) is deposited so as to have a sufficient thickness larger than the sum of the depth of the trench 51 and the thickness of the remaining polysilicon film 4, namely, the height from the bottom of the trench 51 to the top surface of the polysilicon film 4. The silicon oxide film 2 is removed by the CMP method until the surface of the polysilicon film 4 is exposed, thereby flattening the top surface of the substrate. Through this procedure, a trench isolation 2 b made of the silicon oxide film is formed in the isolation region Reiso. The flattening method to be adopted is not limited to that described above but the surface can be flattened by etch-back using a resist film having a reverse pattern to the pattern of the transistor region Refet.

[0190] Next, as is shown in FIG. 14(b), a conductive film 18 serving as a gate interconnection layer (which can be made of a conductive polysilicon film; a silicide film of WSi, TiSi or the like; or a metal with a high melting point such as W with a sandwiched barrier metal such as TiN for achieving low resistance) and a protection film 19 made of an insulating film are deposited on the flattened substrate. Then, a resist film 50 b for exposing an area excluding the areas for a gate electrode and a gate interconnection is formed. By using the resist film 50 b as a mask, dry etching is conducted, thereby forming a gate electrode 4 a, an upper gate electrode 18 a and a protection film 19 a, a gate interconnection 4 b, an upper gate interconnection 18 b and a protection film 19 b, which procedures are not shown in the drawing. At this point, a step portion having a sufficient level difference between the surfaces of the silicon substrate 1 in the transistor region Refet and the isolation 2 b is exposed characteristically in this embodiment. The level difference is approximately 50 through 100 nm in consideration of the amount of over-etch in the subsequent procedure for forming sidewalls and the like. However, in order to effectively achieve the effects of this embodiment, the thickness of an insulating film for the sidewall and the amount of over-etch are required to be appropriately determined in the subsequent procedure for forming the sidewalls.

[0191] Then, as is shown in FIG. 14(c), similarly to Embodiment 8, after forming a low-concentration source/drain region 6 on either side of the gate electrode 4 a in the active area, an insulating film 7 (silicon oxide film) is deposited on the entire top surface of the substrate.

[0192] Next, as is shown in FIG. 14(d), the insulating film 7 is anisotropically etched, thereby forming electrode sidewalls 7 a on both side surfaces of the gate electrode 4 a and the like and interconnection sidewalls 7 b on both side surfaces of the gate interconnection 4 b and the like. At the same time, a step sidewall 7 c is formed on the side surface of the step portion between the silicon substrate 1 in the transistor region Refet and the isolation 2 b. After forming these sidewalls, impurity ions are injected, thereby forming a high-concentration source/drain region 8. Also at this point, the step portion between the silicon substrate 1 in the transistor region Refet and the isolation 2 b has a sufficient level difference.

[0193] Next, as is shown in FIG. 14(e), a source/drain electrode 9 c is formed out of silicide only on the high-concentration source/drain region 8.

[0194] Although the procedures thereafter are not shown in the drawing, an interlayer insulating film 11 is deposited, a contact hole is formed, and the contact hole is filled with a metal (such as tungsten), and a first layer metallic interconnection 12 is formed. Thus, a MOS transistor having a trench isolation similar to that shown in FIG. 12 is manufactured. In this embodiment, however, on the gate electrode 4 a and the gate interconnection 4 b are formed the upper gate electrode 18 a and the upper gate interconnection 18 b made of conductive polysilicon, silicide or the like as well as the protection films 19 a and 19 b made of the insulating film, respectively. The source/drain electrode 9 c of silicide is formed in the procedure different from that for forming the upper gate electrode 18 a and the upper gate interconnection 18 b.

[0195] In this manner, the step portion which is higher at the side closer to the isolation 2 b is formed between the silicon substratel in the transistor region Refet and the isolation 2 b, and the step portion is provided with the step sidewall 7 c on its side surface in this embodiment. Therefore, the same effects as those of Embodiment 8 can be exhibited with a reduced number of manufacturing procedures.

[0196] In addition, the procedure for forming the gate electrode 4 a and the gate interconnection 4 b after the procedure shown in FIG. 14(b) can be conducted on the completely flat top surface of the substrate without being affected by the step portion at the edge of the isolation 2 b in this embodiment. Therefore, a refined pattern can be advantageously stably formed.

[0197] (Embodiment 10)

[0198] Embodiment 10 will now be described referring to FIGS. 15(a) through 15(f), which are sectional views for showing manufacturing procedures for a semiconductor device of this embodiment.

[0199] Before achieving the state shown in FIG. 15(a), a trench isolation 2 b, a channel stop region 60, a low-concentration source/drain region 6, a gate insulating film 3, a gate electrode 4 a, a gate interconnection 4 b and the like are formed through the same procedures as those described in Embodiment 8. Then, a protection oxide film 31, a silicon nitride film 32 for sidewalls and a polysilicon film 33 for a mask are deposited on the substrate by the CVD method. At this point, the thickness of a polysilicon film to be used as the gate electrode 4 a and the gate interconnection 4 b is 330 nm, and the minimum line width is 0.35 μm. The protection oxide film 31 has a thickness of approximately 20 nm, the silicon nitride film 32 has a thickness of approximately 30 nm, and the polysilicon film 33 has a thickness of approximately 100 nm.

[0200] Then, as is shown in FIG. 15(b), the polysilicon film 33 is etched back by RIE (reactive ion etching), thereby forming electrode polysilicon masks 33a, interconnection polysilicon masks 33 b and a step polysilicon mask 33 c on side surfaces of the gate electrode 4 a, the gate interconnection 4 b and a step portion of the isolation 2 b, respectively. At this point, the etching selectivity between the polysilicon film 33 and the silicon nitride film 32 is large.

[0201] Next, as is shown in FIG. 15(c), by using the remaining polysilicon masks 33 a, 33 b and 33 c as masks, wet etching using heated phosphoric acid (H₃PO₄) at 150° C. is conducted, so as to have portions of the silicon nitride film 32 covered with the polysilicon masks 33 a, 33 b and 33 c remained and remove the other portions thereof. At this point, the etching selectivity between the silicon nitride film 32 and the polysilicon masks 33 a, 33 b and 33 c can be approximately 30:1. Through this procedure, electrode sidewalls 32 a, interconnection sidewalls 32 b and a step sidewall 32 c each having an L-shape remain on the sides of the gate electrode 4 a, the gate interconnection 4 b and the step portion, respectively.

[0202] Then, as is shown in FIG. 15(d), by using the gate electrode 4 a, the protection oxide film 31, the electrode polysilicon mask 33 a, the electrode sidewall 32 a, the step polysilicon mask 33 c and the step sidewall 32 c as masks, impurity ions are injected at a high concentration into the active area of the silicon substrate 1, thereby forming a high-concentration source/drain region 8.

[0203] Then, as is shown in FIG. 15(e), the polysilicon masks 33 a, 33 b and 33 c are removed by dry or wet etching.

[0204] Next, as is shown in FIG. 15(f), exposed portions of the protection oxide film 31 on the substrate are removed by using a HF type etching solution. Then, a titanium film is deposited and a first RTA treatment is conducted, thereby forming a silicide layer of a TiSi₂ film through the reaction between titanium and silicon. The titanium film is then removed, and a second RTA treatment is conducted, so that an upper electrode 9 a, an upper interconnection 9 b and a source/drain electrode 9 c each of a silicide layer with a low resistance are formed on the gate electrode 4 a, the gate interconnection 4 b and the source/drain region 8, respectively. Thereafter, an interlayer insulating film is deposited, the top surface of the substrate is flattened, a contact hole is formed, a metallic interconnection film is deposited, and a metallic interconnection is formed. Thus, an LSI is manufactured.

[0205] Since the protection oxide film 31 and the L-shaped step sidewall 32 c are formed on the side surface of the step portion in the procedure shown in FIG. 15(f) in this embodiment, the silicide layer is effectively prevented from being formed in the boundary between the active area of the silicon substrate 1 and the isolation 2 b.

[0206] Furthermore, since the protection oxide film 31 is formed on the isolation 2 b and the active area of the silicon substrate 1 in the procedures shown in FIGS. 15(c) and 15(d), the thickness of the isolation 2 b is never decreased through the formation of the L-shaped sidewalls 32 a, 32 b and 32 c. Accordingly, it is possible to decrease the level difference between the isolation 2 b and the silicon substrate 1, resulting in improving the patterning accuracy for the gate.

[0207] In the formation of the gate electrode, first and second conductive films can be used similarly to Embodiment 2. Also in this case, the same effects as those of this embodiment can be exhibited.

[0208] (Embodiment 11)

[0209] In each of the aforementioned embodiments, each sidewall is made of an insulating material such as a silicon oxide film and a silicon nitride film. The sidewall can be made of a conductive material such as a polysilicon film. FIG. 16(a) through 16(e) are sectional views for showing manufacturing procedures for a semiconductor device including conductive sidewalls.

[0210] Before attaining the state shown in FIG. 16(a), a trench isolation 2 b, a channel stop region 60, a low-concentration source/drain region 6, a gate insulating film 3, a gate electrode 4 a, a gate interconnection 4 b and the like are formed through the same procedures as those described in Embodiment 8. Then, a protection oxide film 31 and a polysilicon film 34 for sidewalls are deposited on the top surface by the CVD method. In this embodiment, on the gate electrode 4 a and the gate interconnection 4 b are formed protection silicon oxide films 15 a and 15 b, respectively. At this point, a polysilicon film to be used as the gate electrode 4 a and the gate interconnection 4 b has a thickness of 330 nm, and the minimum line width is 0.35 μm. The protection oxide film 31 has a thickness of approximately 20 nm and the polysilicon film 34 has a thickness of approximately 100 nm.

[0211] Next, as is shown in FIG. 16(b), the polysilicon film 34 is etched back by the RIE, thereby forming electrode sidewalls 34 a, interconnection sidewalls 34 b and a step sidewall 34 c each made of the polysilicon film on sides of the gate electrode 4 a, the gate interconnection 4 b and a step portion of the isolation 2 b, respectively.

[0212] Next, as is shown in FIG. 16(c), by using the gate electrode 4 a, the protection oxide film 31, the electrode sidewalls 34 a and the step sidewall 34 c as masks, impurity ions are injected at a high concentration into an active area of the silicon substrate 1, thereby forming a high-concentration source/drain region 8.

[0213] Then, as is shown in FIG. 16(d), exposed portions of the protection oxide film 31 on the substrate are removed by using the HF type etching solution. Then, as is shown in FIG. 16(e), a titanium film is deposited and a first RTA treatment is conducted, thereby forming a silicide layer made of a TiSi₂ film through the reaction between titanium and silicon. The titanium film is then removed and a second RTA treatment is conducted, thereby forming a source/drain electrode 9 d made of a silicide layer stretching over the electrode sidewall 34 a, the high-concentration source/drain region 8 and the step sidewall 34 c. Since the silicide layer is formed also on the interconnection sidewall 34 b, this silicide layer can be connected with the source/drain electrode. Therefore, in this embodiment, etching is conducted on the isolation 2 b by using a resist film or the like, so as to selectively remove the interconnection sidewalls 34 b on the sides of the gate interconnection 4 b as well as the silicide layer thereon. Thus, the source/drain electrodes 9 d in the respective active areas are prevented from being mutually connected. It is possible to selectively remove merely the interconnection sidewalls 34 b on the sides of the gate interconnection 4 b immediately after forming the sidewalls 34 a, 34 b and 34 c of the polysilicon film.

[0214] Thereafter, an interlayer insulating film is deposited, the top surface of the substrate is flattened, a contact hole is formed, a metallic interconnection film is deposited, and a metallic interconnection is formed. Thus, an LSI is manufactured.

[0215] In this embodiment, the source/drain electrode 9 d is ultimately formed so as to stretch over a large area including the electrode sidewall 34 a, the high-concentration source/drain region 8 and the step sidewall 34 c. Accordingly, the level difference between the transistor region Refet and the isolation 2 b can effectively prevent the high-concentration source/drain region 8 from being brought close to the channel stop region 60 in the impurity ion injection. Furthermore, in the formation of the source/drain electrode 9 d of silicide on the high-concentration source/drain region 8, also the step sidewall 34 c is silicified by a certain thickness. However, since the silicide layer is prevented from being formed in a further thickness, a short circuit current between the source/drain electrode 9 d and the channel stop region 60 is effectively prevented from being caused by the formation of the silicide layer in the interface between the isolation and the silicon substrate. Moreover, since the large area stretching over the electrode sidewall 34 a, the high-concentration source/drain region 8 and the step sidewall 34 c is silicified in this embodiment, it is very easy to form a contact member to be connected with an upper first layer interconnection. As a result, the area of the transistor region Refet can be decreased, namely, the integration of the semiconductor device can be advantageously improved. Although the electrode sidewalls 34 a and the interconnection sidewalls 34 b are made of a conductive polysilicon film, there is no possibility of a short circuit between the sidewall and the gate because the respective sidewalls 34 a and 34 b are insulated from the gate electrode 4 a and the gate interconnection 4 b by the protection oxide film 31.

[0216] In the formation of the gate electrode, first and second conductive films can be used similarly to Embodiment 9, and also in this case, the same effects as those of this embodiment can be attained.

[0217] The sidewalls are made of a polysilicon film in this embodiment, and the polysilicon film can be replaced with an amorphous silicon film. Furthermore, the sidewalls can be made not only of a silicon film but also of another conductive material such as a metal, and it is not necessarily required to silicify the sidewalls.

[0218] In each of the aforementioned embodiments, the description is made on the case where the semiconductor element formed in the active area is a field effect transistor. However, the invention is not limited to these embodiments, and is applicable when the semiconductor element is a bipolar transistor and the active area is an emitter diffused layer, a collector diffused layer or a base diffused layer of the bipolar transistor.

[0219] In each embodiment, setting of an angle of the side surface of the step portion to be equal to or more than 70° ensures a large level difference between the active area and the side surface of the step portion around the boundary of the active area, thereby preventing formation of a deep recess on the isolation. 

What is claimed is:
 1. A semiconductor device in which a semiconductor element is disposed in each of plural active areas in a semiconductor substrate comprising: an isolation for surrounding and isolating each active area, the isolation having a top surface at a higher level than a surface of the active area and having a step portion in a boundary with the active area; an insulating film formed so as to stretch over each active area and the isolation; plural holes each formed by removing a portion of the insulating film disposed at least on the active area; plural buried conductive layers filled in the respective holes; and plural interconnection members formed on the insulating film so as to be connected with the respective active areas through the respective buried conductive layers.
 2. The semiconductor device of claim 1 , wherein at least a part of the plural holes are formed by also removing another portion of the insulating film disposed on the isolation due to fluctuation in manufacturing procedures.
 3. The semiconductor device of claim 1 , wherein dimensions and materials of respective components are determined so as to satisfy the following inequality: OE x a x (ER2/ER1)<b+D x (2/10) wherein “a” indicates a thickness of the insulating film, “b” indicates a level difference between the surface of the active area and the top surface of the isolation, “ER1” indicates an etching rate of the insulating film in forming the holes, “ER2” indicates an etching rate of the isolation in forming the holes, “D” indicates a depth of an impurity diffused layer in the active area, and “OE” indicates an over-etch ratio of the insulating film in forming the holes.
 4. The semiconductor device of claim 1 , wherein an angle between a side surface of the step portion and the surface of the active area is 70 degrees or more.
 5. The semiconductor device of claim 1 , wherein the isolation is a trench isolation made of an insulating material filled in a trench formed by trenching the semiconductor substrate by a predetermined depth.
 6. The semiconductor device of claim 1 , wherein the semiconductor element is a MISFET including: a gate insulating film and a gate electrode formed on the active area; and source/drain regions formed in the active area on both sides of the gate electrode.
 7. The semiconductor device of claim 6 further comprising a gate interconnection made of a material the same as a material for the gate electrode and formed on the isolation, wherein each of the holes is formed on an area including the source/drain region, the isolation and the gate interconnection, and the plural interconnection members are connected with the gate interconnection on the isolation.
 8. The semiconductor device of claim 6 further comprising: electrode sidewalls made of an insulating material and formed on both side surfaces of the gate electrode; and a step sidewall made of a material the same as the insulating material for the electrode sidewalls and formed on a side surface of the step portion, wherein at least a part of the holes are formed by also removing a portion of the insulating film disposed on the step sidewall.
 9. The semiconductor device of claim 6 further comprising a gate protection film formed on the gate electrode, wherein at least a part of the holes are formed so as to stretch over the source/drain region and at least a part of the gate protection film.
 10. The semiconductor device of claim 9 , wherein dimensions and materials of respective components are determined so as to satisfy the following inequality: OE x a x (ER3/ER1)<c wherein “a” indicates a thickness of the insulating film, “c” indicates a thickness of the gate protection film, “ER1” indicates an etching rate of the insulating film in forming the holes, “ER3” indicates an etching rate of the gate protection film in forming the holes, and “OE” indicates an over-etch ratio of the insulating film in forming the holes.
 11. The semiconductor device of claim 6 , wherein the interconnection members are local interconnections.
 12. The semiconductor device of claim 6 , wherein the interconnection members are first layer metallic interconnections, and the insulating film is an interlayer insulating film disposed between the semiconductor substrate and the first layer metallic interconnections.
 13. The semiconductor device of claim 12 further comprising, between the interlayer insulating film and the semiconductor substrate, an underlying film made of an insulating material having high etching selectivity against the interlayer insulating film.
 14. A semiconductor device in which a semiconductor element is disposed in each of plural active areas in a semiconductor substrate comprising: a trench isolation for isolating and surrounding each active area, the trench isolation having a top surface at a higher level than a surface of the active area and having a step portion in a boundary with the active area; and a step sidewall formed on a side surface of the step portion of the trench isolation.
 15. The semiconductor device of claim 14 , wherein the step sidewall is made of an insulating material.
 16. The semiconductor device of claim 14 , wherein the semiconductor element is a MISFET including: a gate insulating film and a gate electrode formed on the active area; and source/drain regions formed in the active area on both sides of the gate electrode, the semiconductor device is further provided with electrode sidewalls formed on both side surfaces of the gate electrode, and the step sidewall is formed simultaneously with the electrode sidewalls.
 17. The semiconductor device of claim 16 further comprising an electrode formed by silicifying at least a portion in the vicinity of the surface of the active area.
 18. A method of manufacturing a semiconductor device in which a semiconductor element is disposed in each of plural active areas in a semiconductor substrate comprising: a first step of forming an isolation in a part of the semiconductor substrate, the isolation having a top surface at a higher level than a surface of the semiconductor substrate and having a step portion in a boundary with the surface of the semiconductor substrate; a second step of introducing an impurity at a high concentration into each active area of the semiconductor substrate surrounded by the isolation; a third step of forming an insulating film on the active area and the isolation; a fourth step of forming, on the insulating film, a masking member having an exposing area above an area at least including a portion of the active area where the impurity at the high concentration is introduced; a fifth step of conducting etching by using the masking member so as to selectively remove the insulating film and form holes; and a sixth step of forming a buried conductive layer by filling the holes with a conductive material and forming, on the insulating film, interconnection members to be connected with the buried conductive layer, wherein, in the fourth step, an alignment margin is not provided for preventing the exposing area of the masking member from including a portion above the isolation when mask shift is caused in photolithography.
 19. The method of manufacturing a semiconductor device of claim 18 , wherein, the fifth step is performed so as to satisfy the following inequality: OE x a x (ER2/ER1)<b+D x (2/10) wherein “a” indicates a thickness of the insulating film, “b” indicates a level difference between the surface of the active area and the top surface of the isolation, “ER1” indicates an etching rate of the insulating film, “ER2” indicates an etching rate of the isolation, “D” indicates a depth of an impurity diffused layer in the active area, and “OE” indicates an over-etch ratio of the insulating film.
 20. The method of manufacturing a semiconductor device of claim 18 , wherein, in the fourth step, the masking member is formed to be positioned with the exposing area thereof including a portion above the isolation when the mask shift is not caused in the photolithography.
 21. The method of manufacturing a semiconductor device of claim 18 , wherein, in the first step, a trench isolation is formed.
 22. The method of manufacturing a semiconductor device of claim 18 , wherein the semiconductor element is a MISFET, the method further includes, before the second step, a step of forming a gate insulating film on the active area, a step of depositing a conductive film on the gate insulating film and a step of forming a gate electrode by patterning the conducive film, and in the second step, the impurity at the high concentration is introduced so as to form a source/drain region.
 23. The method of manufacturing a semiconductor device of claim 22 , wherein, in the step of forming the gate electrode, a gate interconnection is simultaneously formed so as to stretch over the conductive film and the isolation, and in the fourth step, the masking member is formed so that the exposing area thereof includes portions above the source/drain region and above the gate interconnection.
 24. The method of manufacturing a semiconductor device of claim 22 further comprising, after the step of forming the gate electrode, a step of depositing an insulating film for sidewalls on the gate electrode, the active area and the isolation, and anisotropically etching the insulating film for the sidewalls, so as to form electrode sidewalls on both side surfaces of the gate electrode and form a step sidewall on a side surface of the step portion in the boundary between the isolation and the active area.
 25. The method of manufacturing a semiconductor device of claim 24 further comprising, after the step of depositing the conductive film, a step of depositing a protection insulating film on the conductive film, wherein, in the step of forming the gate electrode, the conductive film as well as the protection insulating film are patterned, so as to form a gate protection film on the gate electrode, and the fifth step is performed so as to satisfy the following inequality: OE x a x (ER3/ER1)<c wherein “a” indicates a thickness of the insulating film, “c” indicates a thickness of the gate protection film, “ER1” indicates an etching rate of the insulating film, “ER3” indicates an etching rate of the gate protection film and “OE” indicates an over-etch ratio of the insulating film.
 26. The method of manufacturing a semiconductor device of claim 25 , wherein, in the fourth step, the masking member is formed to be positioned without providing a margin for preventing the exposing area thereof from including a portion above the gate protection film even when the mask shift is caused in the photolithography.
 27. The method of manufacturing a semiconductor device of claim 25 , wherein, in the fourth step, the masking member is formed to be positioned with the exposing area thereof including at inleast a part of a portion above the gate protection film when the mask shift is not caused in the photolithography.
 28. The method of manufacturing a semiconductor device of claim 22 , wherein, in the sixth step, local interconnections are formed as the interconnection members.
 29. The method of manufacturing a semiconductor device of claim 22 , wherein, in the third step, an interlayer insulating film is formed as the insulating film, and in the sixth step, first layer metallic interconnections are formed as the interconnection members.
 30. The method of manufacturing a semiconductor device of claim 29 , wherein, in the third step, after an underlying film made of an insulating material having high etching selectivity against the interlayer insulating film is formed below the interlayer insulating film, the interlayer insulating film is formed.
 31. A method of manufacturing a semiconductor device comprising: a first step of forming an underlying insulating film on a semiconductor substrate; a second step of depositing an etching stopper film on the underlying insulating film; a third step of forming a trench by exposing a portion of the etching stopper film and the underlying insulating film where an isolation is to be formed and etching the semiconductor substrate in the exposed portion; a fourth step of depositing an insulating film for isolation on an entire top surface of the substrate, flattening the substrate until at least a surface of the etching stopper film is exposed, and forming a trench isolation in the trench so as to surround a transistor region; a fifth step of removing, by etching, at least the etching stopper film and the underlying insulating film, so as to expose a step portion between the transistor region and the trench isolation; a sixth step of depositing a gate oxide film and a conductive film on the substrate and making the conductive film into a pattern of at least a gate electrode; a seventh step of depositing an insulating film for sidewalls on the entire top surface of the substrate and anisotropically etching the insulating film for the sidewalls, so as to form electrode sidewalls and a step sidewall on side surfaces of the gate electrode and the step portion, respectively; and an eighth step of introducing an impurity into the semiconductor substrate in the transistor region on both sides of the gate electrode, so as to form source/drain regions.
 32. The method of manufacturing a semiconductor device of claim 31 , wherein, in the second step, a thickness of the etching stopper film is determined in consideration of an amount of over-etch in the seventh step, so that the step portion having a level difference with a predetermined size or more is exposed in the fifth step.
 33. The method of manufacturing a semiconductor device of claim 31 further comprising, after completing the eighth step, a step of silicifying at least an area in the vicinity of the surface of the source/drain region.
 34. The method of manufacturing a semiconductor device of claim 31 , wherein, in the sixth step, a first protection insulating film is deposited on the conductive film, and the first protection insulating film as well as the gate electrode are made into the pattern, the method further includes, after the sixth step and before the seventh step, a step of depositing a second protection insulating film on the entire top surface of the substrate, in the seventh step, a silicon film is deposited as the insulating film for the sidewalls, and the method further includes, after the eighth step, a step of silicifying an area stretching over the electrode sidewall, the active area and the step sidewall.
 35. A method of manufacturing a semiconductor device comprising: a first step of forming a gate insulating film on a semiconductor substrate; a second step of depositing a first conductive film to be formed into a gate electrode on the gate insulating film; a third step of forming a trench by exposing a portion of the first conductive film where a trench isolation is to be formed and etching the semiconductor substrate in the exposed portion; a fourth step of depositing an insulating film for isolation on an entire top surface of the substrate, flattening the substrate at least until a surface of the first conductive film is exposed, and forming the trench isolation in the trench so as to surround a transistor region; a fifth step of depositing a second conductive film to be formed into at least an upper gate electrode on the entire top surface of the flattened substrate; a sixth step of making the first and second conductive films into a pattern at least of the gate electrode and exposing a step portion between the transistor region and the trench isolation; a seventh step of depositing an insulating film for sidewalls on the entire top surface of the substrate and anisotropically etching the insulating film for the sidewalls, so as to form electrode sidewalls and a step sidewall on side surfaces of the gate electrode and the step portion, respectively; and an eighth step of introducing an impurity into the semiconductor substrate in the transistor region on both sides of the gate electrode, so as to form source/drain regions.
 36. The method of manufacturing a semiconductor device of claim 35 , wherein, in the second step, a thickness of the first conductive film is determined in consideration of at least an amount of over-etch in the seventh step, so that the step portion having a level difference with a predetermined size or more is exposed in the sixth step.
 37. The method of manufacturing a semiconductor device of claim 35 further comprising, after completing the eighth step, a step of silicifying at least a portion in the vicinity of the surface of the active area.
 38. The method of manufacturing a semiconductor device of claim 35 , wherein, in the sixth step, a first protection insulating film is deposited on the conductive film and the first protection insulating film as well as the gate electrode are made into the pattern, the method further includes, after the sixth step and before the seventh step, a step of depositing a second protection insulating film on the entire top surface of the substrate, in the seventh step, a silicon film is deposited as the insulating film for the sidewalls, and the method further includes, after the eighth step, a step of silicifying an area stretching over the electrode sidewall, the source/drain region and the step sidewall. 